EVA Foam / PE Foam Properties Table
Following data tables are in both unit systems:
► Units in SI system ( International System of Units, i.e. kg, g, m, cm, mm, ... )
► Units in EES system ( English Engineering System, i.e. lb, ft, inch, ... )
|
Item No.
|
L-2500
|
C-1600
|
C-3000
|
H-25
|
|
A-25
|
Density ( g/cm^3 )
Density ( lb/ft^3 )
|
0.021~0.027
1.3~1.7
|
0.035~0.041
2.2~2.6
|
0.023~0.029
1.4~1.8
|
0.065~0.075
4.1~4.7
|
0.07~0.08
4.4~5.0
|
0.08~0.09
5.0~5.6
|
Hardness (durometer type C)
|
15~21
|
24~30
|
7~13
|
25~30
|
30~35
|
25~30
|
Original Sheet Size
cm ( inch )
|
100 x 200
(39.4"x78.7")
|
100 x 200
(39.4"x78.7")
|
100 x 200
(39.4"x78.7")
|
100 x 200
(39.4"x78.7")
|
100 x 200
(39.4"x78.7")
|
100 x 200
(39.4"x78.7")
|
Original Sheet Thickness
mm ( inch )
|
80mm
( 3.15" )
|
80mm
( 3.15" )
|
80mm
( 3.15" )
|
36mm
( 1.42" )
|
32mm
( 1.26" )
|
38mm
( 1.50" )
|
Tensile Strength
( kg/cm^2 )
( PSI, lb/in^2 )
|
2.0
28.5
|
3.2
45.5
|
2.8
39.8
|
9.5
135.1
|
11.8
167.9
|
9.5
135.1
|
Elongation at Break ( % )
|
180
|
180
|
340
|
220
|
160
|
120
|
Tear Strength
( kg/cm )
( lb/in )
|
1.9
10.6
|
2.4
13.4
|
2.1
11.8
|
3.4
19.0
|
3.8
21.3
|
3.3
18.5
|
Compressive Strength
at 25% Deflection
( kg/cm^2 )
( lb/in^2, PSI )
|
0.4
5.7
|
0.6
8.5
|
0.3
4.3
|
0.7
10.0
|
0.8
11.4
|
0.7
10.0
|
Compressive Strength
at 50% Deflection
( kg/cm^2 )
( lb/in^2, PSI )
|
1.0
14.2
|
1.3
18.5
|
0.8
11.4
|
1.5
21.3
|
1.8
25.6
|
1.6
22.8
|
Compression Set to 50%
of Original Thickness ( % )
|
10
|
14
|
17
|
20
|
20
|
20
|
Water Absorption
( %, by weight, room temp.,
5 hours )
|
< 1
|
< 1
|
< 1
|
< 1
|
< 1
|
< 1
|
Resin Type
|
PE/EVA
|
PE/EVA
|
EVA/PE
|
EVA/PE
|
EVA/PE
|
EVA
|
| Color(s) Available |
C
|
C
|
C
|
B/W/G, C
|
R, C
|
B/W/G, C
|
|
Item No.
|
|
|
B-20HV
|
P-560
|
P-565
|
Density ( g/cm^3 )
Density ( lb/ft^3 )
|
0.075~0.085
4.7~5.3
|
0.075~0.085
4.7~5.3
|
0.11~0.115
6.7~7.2
|
0.125~0.135
7.8~8.4
|
0.17~0.18
10.6~11.2
|
Hardness (durometer type C)
|
32~38
|
45~50
|
20~25
|
55~60
|
60~65
|
Original Sheet Size
cm ( inch )
|
100 x 200
(39.4"x78.7")
|
94 x 188
(37.0"x74.0")
100 x 200
(39.4"x78.7")
|
100 x 200
(39.4"x78.7")
|
90 x 180
(35.4"x70.9")
110 x 235
(43.3"x92.5")
|
100 x 190
(39.4"x74.8")
100 x 220
(39.4"x86.6")
|
Original Sheet Thickness
mm ( inch )
|
24mm
( 0.94" )
|
32mm
( 1.26" )
40mm
( 1.57" )
|
43mm
( 1.69" )
|
32mm
( 1.26" )
|
28mm
( 1.10" )
|
Tensile Strength
( kg/cm^2 )
( PSI, lb/in^2 )
|
9.4
133.7
|
13.0
184.9
|
9.3
132.3
|
18.8
267.4
|
26.4
375.6
|
Elongation at Break ( % )
|
90
|
130
|
140
|
120
|
150
|
Tear Strength
( kg/cm )
( lb/in )
|
3.2
17.9
|
3.3
18.5
|
2.8
15.7
|
5.6
31.4
|
8.3
46.5
|
Compressive Strength
at 25% Deflection
( kg/cm^2 )
( lb/in^2, PSI )
|
0.8
11.4
|
0.9
12.8
|
0.5
7.1
|
0.8
11.4
|
1.4
19.9
|
Compressive Strength
at 50% Deflection
( kg/cm^2 )
( lb/in^2, PSI )
|
1.5
21.3
|
1.5
21.3
|
1.2
17.1
|
1.3
18.5
|
2.4
34.1
|
Compression Set to 50%
of Original Thickness ( % )
|
10
|
30
|
20
|
2
|
1
|
Water Absorption
( %, by weight, room temp.,
5 hours )
|
< 1
|
< 1
|
< 1
|
< 1
|
< 1
|
Resin Type
|
PE/EVA
|
PE/EVA
|
EVA
|
EVA/PE
|
EVA/PE
|
Color(s) Available
|
R, C
|
R, C
|
BL
|
B/W/G, C
|
C
|
Above information is for reference only, actual production may slightly vary.
Ver. 130501-101230